News Release

Uncovering the superconducting phosphine: P2H4 and P4H6

Peer-Reviewed Publication

Science China Press

Figure 1

image: The high pressure phase diagrams of PH3 at room temperature and low temperature. view more 

Credit: ©Science China Press

Searching high-Tc superconductor has become a hot topic in physics since superconducting mercury was first reported more than one century ago. Dense hydrogen was predicted to metalize and become superconductor at high pressure and room temperature. However, it has been very challenging and no widely accepted experimental work has been reported yet. In 2004, Ashcroft predicted hydrogen-dominant hydrides could become high-Tc superconductor at high pressure, due to the 'chemical precompression'. Later, Drozdov et al. observed the superconductive transition of H2S at 203 K and 155 GPa, which broke the highest Tc record. Very recently, LaH6 was reported to shown superconducting behavior at ~260K. Motivated by these works, extensive investigations on hydrides system have been reported.

PH3, a typical hydrogen-rich hydride, has attracted a great deal of research interest because of its superconducting transition discovered at high pressure. However, structural information was not provided, and the origin of the superconducting transition remains puzzling. Although a series of theoretical works suggested possible structures, the PH3 phase under compression has remained unknown and no relevant experimental studies have been reported.

In a recent research article published in National Science Review, scientists from the Center for High Pressure Science and Technology Advanced Research, School of Physics and Electronic Engineering, Jiangsu Normal University, Key Laboratory of Carbon Materials of Zhejiang Province, College of Chemistry and Materials Engineering, Wenzhou University and Shanghai Institute of Applied Physics, Chinese Academy of Sciences present their results on the studies of stoichiometric evolutions of PH3 under high pressure. It was found that PH3 is stable below 11.7 GPa and then it starts to dehydrogenate through two dimerization processes at room temperature and pressures up to 25 GPa. Two resulting phosphorus hydrides, P2H4 and P4H6, were verified experimentally and can be recovered to ambient pressure. Under further compression above 35 GPa, the P4H6 directly decomposed into elemental phosphorus. Low temperature can greatly hinder polymerization/decomposition under high pressure, and retain P4H6 up to at least 205 GPa. "Our findings suggested that P4H6 might be responsible for superconductivity at high pressures." said Dr. Lin Wang, the corresponding author of the article.

To determine the possible structure of P4H6 at high pressure, structural searches were further performed. Theoretical calculations revealed that two stable structures with space group Cmcm (< 182 GPa) and C2/m (> 182 GPa) were found. Phonon dispersions calculations of the two structures do not give any imaginary frequencies and therefore, this verifies their dynamic stabilities. The superconducting Tc of the C2/m structure at 200 GPa was estimated to be 67 K. "All of these findings confirmed P4H6 might be the corresponding superconductor, which is helpful for shedding light on the superconducting mechanism." Dr. Wang added.

###

This work was mainly supported by Natural Science Foundation of China (Grant No. 11874076), National Science Associated Funding (NSAF, Grant No. U1530402) and Science Challenging Program (Grant No. JCKY2016212A501).

See the article:

Ye Yuan, Yinwei Li, Guoyong Fang, Guangtao Liu, Cuiying Pei, Xin Li, Haiyan Zheng, Ke Yang, Lin Wang

Stoichiometric evolutions of PH3 under high pressure: implication for high Tc superconducting hydrides

Natl Sci Rev, https://doi.org/10.1093/nsr/nwz010

The National Science Review is the first comprehensive scholarly journal released in English in China that is aimed at linking the country's rapidly advancing community of scientists with the global frontiers of science and technology. The journal also aims to shine a worldwide spotlight on scientific research advances across China.


Disclaimer: AAAS and EurekAlert! are not responsible for the accuracy of news releases posted to EurekAlert! by contributing institutions or for the use of any information through the EurekAlert system.