A novel thermal insulation material for ultra-high temperature applications: Hierarchical porous (Ta0.2Nb0.2Ti0.2Zr0.2Hf0.2)C high-entropy ceramics

Thermal insulation material is a critical part in thermal protection system (TPS) of the hypersonic vehicles. Recently, high-entropy ceramics has attracted great attentions in thermal insulation for their low thermal conductivity due to the scattering of phonons by multi-components and distorted lattices. Among the various options available, porous high-entropy carbide (PHEC) ceramics have emerged as promising candidates for TPS due to their inherent characteristics such as high melting point, excellent high-temperature stability, low density, and superior thermal insulation properties.

Generally, porous high-entropy carbide ceramics have been fabricated using various methods such as template, direct foaming, and partial sintering. To synthesize these ceramics, metal carbides or oxides are commonly used as starting materials by solid-state methods. This requires extensive milling to disperse the various components and extremely high processing temperatures to accelerate the diffusion of atoms. However, this approach is energy-intensive and introduces impurities during the ball milling process, which destroys the stoichiometry and affects configurational entropy. Additionally, high-temperature sintering results in grain growth and the elimination of nanosized pores, making it difficult to regulate the porosity and pore structure of the PHEC ceramic. Moreover, the molding and processing of high-entropy carbides is limited by this solid-state method.

 

Recently, a team of material scientists led by Haibo Ouyang from Shaanxi University of Science and Technology, China reported the fabrication, microstructure, compressive strength and thermal conductivity of the porous (Ta_0.2Nb_0.2Ti_0.2Zr_0.2Hf_0.2)C high-entropy ceramics by a self-foaming method.

 

This work not only explains the formation mechanism of the unique hierarchical porosity structure and superior compressive and thermal insulation properties of the porous (Ta_0.2Nb_0.2Ti_0.2Zr_0.2Hf_0.2)C high-entropy ceramics, but also provides a cost-effective and facility strategy to produce porous ultrahigh temperature ceramics.

 

The team published their work in Journal of Advanced Ceramics on May 6, 2024.

 

“In this report, we synthesized the porous (Ta_0.2Nb_0.2Ti_0.2Zr_0.2Hf_0.2)C high-entropy ceramics by a self-foaming method using commercially available metal chloride and furfuryl alcohol as the precursor. This method was inspired by the self-foaming behavior of FA. The polymer foam that contains elements like Ti, Zr, Ta, Nb, and Hf can be produced by the self-condensation of FA using metal chlorides as catalysts. The polymer foam transformed into porous ceramics through pyrolysis and carbothermal reduction processes.” said Haibo Ouyang, professor at School of Materials Science and Engineering at Shaanxi University of Science and Technology (China), an expert whose research interests focus on the field of ultra-high temperature ceramics material and composites.

 

“The PHEC ceramic is constructed by microspheres with a size of 2 µm, leading to a high porosity of 91.3% and an interconnected frame. These microspheres consist of high-entropy carbide grains (20 nm), resulting in abundant interface and nanosized pores in the PHEC ceramic.” said Ouyang.

 

“Due to its unique hierarchical structure, the prepared PHEC ceramic has outstanding compressive strength (28.1±2 MPa) and exceptionally low thermal conductivity at room temperature (0.046 W·m−1·K−1). This makes it a promising thermal insulation material in ultrahigh temperature application.” said Ouyang.

 

However, more delicate research works are still needed to explore the oxidation resistance of the porous (Ta_0.2Nb_0.2Ti_0.2Zr_0.2Hf_0.2)C high-entropy ceramics as a new thermal insulation material. In this regard, Ouyang also put forward two major works including the oxidation/ablation resistance in ultrahigh-temperature and high temperature mechanical properties.

 

Other contributors include Cuiyan Li, Ruinan Gao, Tianzhan Shen, Zihao Chen, Yanlei Li from the School of Materials Science and Engineering at Shaanxi University of Science and Technology, China.

 

This work was supported by the National Natural Science Foundation of China (Nos. 52173299 and 52372087) and the Natural Science Foundation of Shaanxi Province (No. 2021JZ-51).

 

---

About Author

Haibo Ouyang is a professor at the School of Materials Science and Engineering, Shaanxi University of Science and Technology. He received his PhD degree in Materials Science from Northwestern Polytechnical University in 2009. He was a visiting scholar at the University of Delaware from 2018 to 2019. His current interests and fields of research are designing, fabrication, and understanding the structural-property relations of ceramics/composites for ultra-high temperature applications.

About Journal of Advanced Ceramics

Journal of Advanced Ceramics (JAC) is an international academic journal that presents the state-of-the-art results of theoretical and experimental studies on the processing, structure, and properties of advanced ceramics and ceramic-based composites. JAC is Fully Open Access, monthly published by Tsinghua University Press, and exclusively available via SciOpen. JAC’s 2023 IF is 18.6, ranking in Top 1 (1/31, Q1) among all journals in “Materials Science, Ceramics” category, and its 2023 CiteScore is 21.0 (top 5%) in Scopus database. ResearchGate homepage: https://www.researchgate.net/journal/Journal-of-Advanced-Ceramics-2227-8508

About SciOpen 

SciOpen is an open access resource of scientific and technical content published by Tsinghua University Press and its publishing partners. SciOpen provides end-to-end services across manuscript submission, peer review, content hosting, analytics, identity management, and expert advice to ensure each journal’s development. By digitalizing the publishing process, SciOpen widens the reach, deepens the impact, and accelerates the exchange of ideas.

---

---