PECS also shows promise in being able to produce high performance porous materials. The difficulty in producing such porous materials is the ability to produce a homogenous microstructure.
In this paper, Japanese researchers, Manabu Sato, Makoto Nanko, Koji Matsumaru and Kozo Ishizaki, from the Nagaoka University of Technology examine density homogeneity in partially–sintered metallic bodies produced using PECS. In order to obtain homogeneous microstructure the effects of geometry of the graphite die is also investigated. Fine Ni-20Cr powder with particle size of 5 µm and coarse powder with 70 µm in particle size were used in order to discuss effects of powder size.
The researchers successfully produced porous bodies using the PECS technology. They found that sintering rates were faster for finer starting powders when compared to coarser powders, with differing dies sizes and geometries making no significant difference. Coarser powders, despite their slower rates of densification produced homogenous microstructures. Finer powders in contrast, were found to be significantly denser on the inside compared to the outside. This was attributed to temperature gradients from Joule heating and heat transfer during the sintering process. The use of die with thicker walls was found to resolve this issue and at the same time improved reproducibility.
The AZojomo* article is available to view at http://www.azom.com/Details.asp?ArticleID=3423
*AZojomo publishes high quality articles and papers on all aspects of materials science and related technologies. All the contributions are reviewed by a world class panel of editors who are experts in a wide spectrum of materials science. [See http://www.azom.com/Journal%20Editorial%20Board.asp]
AZojomo is based on the patented OARS (Open Access Rewards System) publishing protocol. The OARS protocol represents a unique development in the field of scientific publishing – the distribution of online scientific journal revenue between the authors, peer reviewers and site operators with no publication charges, just totally free to access high quality, peer reviewed materials science. [See http://www.azom.com/azojomo.asp and http://www.azom.com/oars.asp]